823GB Cover-Coat For Rubber Composite Pipes Of Mining Machine

823GB Cover-Coat For Rubber Composite Pipes Of Mining Machine

(Equivalent to Chemlok 220LF/6125/6220, Chemosil 225/222/222NL, Thixon 520/526)

Description:

Rubber to metal bonding agent 823GB is multifunctional adhesive suitable for bonding various elastomercompounds to substrates during the vulcanization process as a cover coat adhesive. It is formulated withoutheavy metals and composed of a mixture of polymers, organic compounds and mineral fillers dissolved ordispersed in an organic solvent system.
This adhesive system will bond compounds based on natural rubber (NR), polyisoprene (IR),styrene-butadiene (SBR), polybutadiene (BR), polychloroprene (CR) and nitrile (NBR) polymers to metal.

Purpose:

Surface treatment agent used for bonding rubber to metal as a cover coat.

Applicable Range:

Used as a cover coat adhesive and in combination with a primer adhesive, suitable for the following types ofrubber:
Natural rubber (NR), Natural & butadiene rubber (NR+BR), Polyisoprene rubber (IR), Butadiene rubber (BR),Chloroprene rubber (CR), Styrene butadiene rubber (SBR), Nitrile butadiene rubber (NBR), etc.

Features and Benefits:

Environmentally friendly, Compliant with GB 33372-2020.
Free of heavy metal elements.
Good construction performance.
Excellent fatigue resistance.
Excellent weather resistance - heat resistance, water resistance, solvent resistance, oil resistance, salt sprayresistance, corrosion resistance.

Performance:
Components: polymers, organic compounds, inorganic fillers and organic solvents.

Typical Properties:

Application:
Stirring: During the storage process of 823GB, some sediment will settle at the bottom of the container.Before painting, it must be thoroughly stirred to achieve uniform mixing before use; If the painting process islong, stir at high speed for 5-10 minutes every 2 hours.
Diluting: This product can also be diluted with diluents according to actual operational needs. It is recommended to dilute according to the amount used. Diluted products should not be stored for a long time.
Brush coating method: no dilution is required, or 100 parts of 823GB and 10 parts of diluent.
Roller coating method: no dilution is required, or 100 parts of 823GB and 10 parts of diluent.
Dip: 100 parts of 823GB and 20-30 parts of diluen.
Spray method: 100 parts of 823GB and 50-100 parts of diluent.
Coating: This product can be coated by brushing, dipping, roller coating, spraying, and other methods. The processing layer should be uniform to avoid excessive overflow.
Cover coating: Dry film thickness(DFT) 10-20μm.
Drying: Drying at room temperature takes about 45-60 minutes, and forced drying can shorten the drying time.
Product storage: This product needs to be stored in a dry room temperature environment to avoid prolonged exposure to high humidity and high temperature environments.
Cleaning: Before heating vulcanization, dip a rag in xylene solvent to remove excess treatment agent spilt around. Once cured, solvent cannot be removed.
Vulcanization: Vulcanization of rubber and adhesive at the same time can obtain the best bonding properties. When the coating is placed in the molding mold, it should be quickly filled with rubber vulcanization. The actual curing condition depends on the curing condition of the rubber.

Shelf Life/Storage:
Shelf life is 12 months from date of shipment when stored at ＜ 37℃ in original, unopened container. Do not store or use near heat, sparks or open flame.

Precautions:
This product is volatile, please close the container after use.
Solvent steam is harmful, pay attention to fire prevention in the workplace, pay attention to low ventilation,prevent long-term inhalation or long-term skin contact.
Please refer to SDS for more safety information.